Fortron? 1140L4

Polyphenylene Sulfide

Celanese Corporation

40% 玻璃纖維增強材料

產(chǎn)品說明：

Fortron 1140L4 is a 40% glass-reinforced grade that is the strongest and toughest product available. It exhibits excellent heat and chemical resistance, good electrical properties and is inherently flame-retardant. The high hardness and rigidity at elevated temperatures allows for good load bearing performance. This product has good weldability due to the modest filler level. Applications made of this grade are electronical components (i.e. bobbins, lamp housings, brush holders) and various other components requiring strength and resistance to aggressive chemicals (i.e. automotive heaters, pumps, valves, fuel rails, microwave oven rings and distillation column packings).

物性信息：

基本信息
黃卡編號

E107854-237735

E107854-237738

E107854-237739

填料/增強材料

玻璃纖維增強材料, 40% 填料按重量

特性

超高韌性

剛性，高

高強度

可焊接

良好的電氣性能

耐化學(xué)性良好

耐熱性，高

硬度高

阻燃性

用途

泵件

電氣/電子應(yīng)用領(lǐng)域

閥門/閥門部件

汽車領(lǐng)域的應(yīng)用

外殼

RoHS 合規(guī)性

聯(lián)系制造商

多點數(shù)據(jù)

Isochronous Stress vs. Strain (ISO 11403-1)

Isothermal Stress vs. Strain (ISO 11403-1)

Shear Modulus vs. Temperature (ISO 11403-1)

物理性能額定值單位制測試方法比重1.65g/cm3ASTM D792, ISO 1183特定體積0.611cm3/gASTM D792充模分析額定值單位制測試方法Specific Heat Capacity of Melt1500J/kg/°C內(nèi)部方法補充信息額定值單位制測試方法Specimen Thickness - Shrinkage3.18mm內(nèi)部方法物理性能額定值單位制測試方法收縮率


    流動0.20 到 0.30%ASTM D955    橫向流動0.50 到 0.70%ASTM D955    垂直流動方向0.40 到 0.60%ISO 294-4    流動方向0.20 到 0.60%ISO 294-4吸水率 (飽和, 23°C)0.020%ISO 62硬度額定值單位制測試方法洛氏硬度


    M 級100
ASTM D785    M 計秤100
ISO 2039-2機械性能額定值單位制測試方法拉伸模量


    -40°C14500MPaASTM D638    75°C11900MPaASTM D638    150°C4270MPaASTM D638    200°C3240MPaASTM D638    --14700MPaISO 527-2/1A/1抗張強度


    斷裂, 23°C200MPaASTM D638    斷裂195MPaISO 527-2/1A/5伸長率


    斷裂, 23°C1.7%ASTM D638    斷裂1.9%ISO 527-2/1A/5彎曲模量 (23°C)14500MPaISO 178彎曲應(yīng)力 1285MPaISO 178沖擊性能額定值單位制測試方法簡支梁缺口沖擊強度

ISO 179/1eA    -30°C10kJ/m2ISO 179/1eA    23°C10kJ/m2ISO 179/1eA簡支梁無缺口沖擊強度

ISO 179/1eU    -30°C53kJ/m2ISO 179/1eU    23°C53kJ/m2ISO 179/1eU懸壁梁缺口沖擊強度

ISO 180/1A    -30°C10kJ/m2ISO 180/1A    23°C10kJ/m2ISO 180/1A無缺口伊佐德沖擊強度 (23°C)34kJ/m2ISO 180/1U熱性能額定值單位制測試方法載荷下熱變形溫度


    0.45 MPa, 退火280°CASTM D648    1.8 MPa, 未退火265°CASTM D648    1.8 MPa, 未退火270°CISO 75-2/A    8.0 MPa, 未退火215°CISO 75-2/C玻璃轉(zhuǎn)化溫度 290.0°CISO 11357-2熔融溫度 3280°CISO 11357-3線形熱膨脹系數(shù)

ISO 11359-2    流動2.6E-5cm/cm/°CISO 11359-2    橫向4.2E-5cm/cm/°CISO 11359-2電氣性能額定值單位制測試方法表面電阻率> 1.0E+15ohmsIEC 60093體積電阻率


    --1.0E+16ohms·cmASTM D257    --> 1.0E+15ohms·cmIEC 60093介電強度28kV/mmIEC 60243-1介電常數(shù)


    1 kHz3.50
ASTM D150    1 MHz3.50
ASTM D150    1 MHz4.60
IEC 60250耗散因數(shù)


    1 kHz1.0E-3
ASTM D150    1 MHz1.0E-3
ASTM D150    1 MHz6.2E-3
IEC 60250耐電弧性134secASTM D495漏電起痕指數(shù)125VIEC 60112可燃性額定值單位制測試方法UL 阻燃等級

UL 94    0.380 mmV-0
UL 94    1.50 mmV-0
UL 94    3.00 mm5VA
UL 94極限氧指數(shù)47%ISO 4589-2注射額定值單位制
干燥溫度130 到 140°C
干燥時間3.0 到 4.0hr
建議的最大水分含量0.020%
料斗溫度20.0 到 30.0°C
料筒后部溫度290 到 300°C
料筒中部溫度310 到 320°C
料筒前部溫度330 到 340°C
射嘴溫度310 到 330°C
加工（熔體）溫度330 到 340°C
模具溫度140 到 160°C
注塑壓力50.0 到 100MPa
注射速度快速

保壓30.0 到 70.0MPa
背壓0.00 到 3.00MPa
注射說明