商品描述價格說明聯(lián)系我們規(guī)格25KG加工定制否有效成分含量PET產品特性阻燃級是否進口是產地美國廠家(產地)美國杜邦牌號FR543NC010銷售方式品牌經(jīng)銷類型標準料品名聚對苯二甲酸乙二醇酯加工級別注塑級產品規(guī)格25KG/包加工方式注射成型顏色本色材料形狀顆粒狀阻燃等級V-05VA可賣售地全國品牌美國杜邦DuPont Performance Polymers Rynite? FR543 NC010 PETPolyethylene Terephthalate (PET), 40% Glass ReinforcedDuPont Performance Polymers產品說明：Rynite? FR543 NC010 is a flame retardant, 43% glass reinforced polyethylene terephthalate. Has a 155C temperature index that is e to many thermosets. Recognized by UL as UL94V-0 at 0.8mm(0.03in).Information provided by DuPont Performance Polymers物性信息：物理性能額定值 (公制)額定值 (英制)測試方法比重1.79 g/cc1.79 g/ccASTM D792密度1.79 g/cc0.0647 lb/in3ISO 1183填料含量43 %43 %Water Absorption0.060 %@Temperature 23.0 °C0.060 %@Temperature 73.4 °F50%RH,23°C,24h; ASTM D5700.11 %@Temperature 23.0 °C0.11 %@Temperature 73.4 °FE 50%RH; ISO 62, Similar to0.62 %@Temperature 23.0 °C0.62 %@Temperature 73.4 °FSaturation, immersed; ISO 62, Similar to線性成型收縮率0.0013 cm/cm@Thickness 1.57 mm0.0013 in/in@Thickness 0.0618 inFlow0.0020 cm/cm@Thickness 3.20 mm0.0020 in/in@Thickness 0.126 inFlow0.0048 cm/cm@Thickness 1.57 mm0.0048 in/in@Thickness 0.0618 inTransverse0.0065 cm/cm@Thickness 3.20 mm0.0065 in/in@Thickness 0.126 inTransverse線性成型收縮率,Flow0.0025 cm/cm0.0025 in/inAnnealed; ISO 294-40.0020 cm/cm@Thickness 2.00 mm0.0020 in/in@Thickness 0.0787 inISO 294-4線性成型收縮率，橫向0.0105 cm/cm0.0105 in/inAnnealed; ISO 294-40.0075 cm/cm@Thickness 2.00 mm0.0075 in/in@Thickness 0.0787 inISO 294-4化合物熔體指數(shù)6.0 g/10 min@Load 2.16 kg, Temperature 280 °C6.0 g/10 min@Load 4.76 lb, Temperature 536 °Fcm3/10 min; ISO 1133機械性能額定值 (公制)額定值 (英制)測試方法洛氏硬度（M 級）9595ASTM DISO 2039/2洛氏硬度（R 級）120120ASTM DISO 2039/2抗張強度(斷裂)170 MPa@Temperature 23.0 °C24700 psi@Temperature 73.4 °FISO 527抗張強度55.2 MPa@Temperature 150 °C8010 psi@Temperature 302 °FASTM D63886.5 MPa@Temperature 90.0 °C12500 psi@Temperature 194 °FASTM D638172 MPa@Temperature 23.0 °C24900 psi@Temperature 73.4 °FASTM D638210 MPa@Temperature -40.0 °C30500 psi@Temperature -40.0 °FASTM D63822.4 MPa@Strain 0.470 %, Temperature 150 °C3250 psi@Strain 0.470 %, Temperature 302 °FISO 52727.22 MPa@Strain 0.430 %, Temperature 120 °C3948 psi@Strain 0.430 %, Temperature 248 °FISO 52727.5 MPa@Strain 0.160 %, Temperature 0.000 °C3990 psi@Strain 0.160 %, Temperature 32.0 °FISO 52728.39 MPa@Strain 0.350 %, Temperature 90.0 °C4118 psi@Strain 0.350 %, Temperature 194 °FISO 52729.0 MPa@Strain 0.140 %, Temperature -40.0 °C4210 psi@Strain 0.140 %, Temperature -40.0 °FISO 52730.0 MPa@Strain 0.210 %, Temperature 40.0 °C4350 psi@Strain 0.210 %, Temperature 104 °FISO 52731.0 MPa@Strain 0.180 %, Temperature 23.0 °C4500 psi@Strain 0.180 %, Temperature 73.4 °FISO 52734.9 MPa@Strain 0.940 %, Temperature 150 °C5060 psi@Strain 0.940 %, Temperature 302 °FISO 52735.57 MPa@Strain 0.310 %, Temperature 60.0 °C5159 psi@Strain 0.310 %, Temperature 140 °FISO 52741.5 MPa@Strain 1.41 %, Temperature 150 °C6020 psi@Strain 1.41 %, Temperature 302 °FISO 52741.8 MPa@Strain 0.830 %, Temperature 120 °C6060 psi@Strain 0.830 %, Temperature 248 °FISO 52745.7 MPa@Strain 1.87 %, Temperature 150 °C6630 psi@Strain 1.87 %, Temperature 302 °FISO 52747.19 MPa@Strain 0.690 %, Temperature 90.0 °C6844 psi@Strain 0.690 %, Temperature 194 °FISO 52749.1 MPa@Strain 2.34 %, Temperature 150 °C7120 psi@Strain 2.34 %, Temperature 302 °FISO 52750.35 MPa@Strain 0.370 %, Temperature 40.0 °C7303 psi@Strain 0.370 %, Temperature 104 °FISO 52750.8 MPa@Strain 1.23 %, Temperature 120 °C7370 psi@Strain 1.23 %, Temperature 248 °FISO 52751.7 MPa@Strain 2.81 %, Temperature 150 °C7500 psi@Strain 2.81 %, Temperature 302 °FISO 52752.4 MPa@Strain 0.320 %, Temperature 0.000 °C7600 psi@Strain 0.320 %, Temperature 32.0 °FISO 52753.8 MPa@Strain 3.28 %, Temperature 150 °C7800 psi@Strain 3.28 %, Temperature 302 °FISO 52753.9 MPa@Strain 0.280 %, Temperature -40.0 °C7820 psi@Strain 0.280 %, Temperature -40.0 °FISO 52755.0 MPa@Strain 0.520 %, Temperature 60.0 °C7980 psi@Strain 0.520 %, Temperature 140 °FISO 52755.6 MPa@Strain 3.75 %, Temperature 150 °C8060 psi@Strain 3.75 %, Temperature 302 °FISO 52756.4 MPa@Strain 0.350 %, Temperature 23.0 °C8180 psi@Strain 0.350 %, Temperature 73.4 °FISO 52756.85 MPa@Strain 1.63 %, Temperature 120 °C8245 psi@Strain 1.63 %, Temperature 248 °FISO 52757.1 MPa@Strain 4.21 %, Temperature 150 °C8280 psi@Strain 4.21 %, Temperature 302 °FISO 52758.5 MPa@Strain 4.69 %, Temperature 150 °C8480 psi@Strain 4.69 %, Temperature 302 °FISO 52759.61 MPa@Strain 1.03 %, Temperature 90.0 °C8646 psi@Strain 1.03 %, Temperature 194 °FISO 52761.26 MPa@Strain 2.04 %, Temperature 120 °C8885 psi@Strain 2.04 %, Temperature 248 °FISO 52764.62 MPa@Strain 2.44 %, Temperature 120 °C9372 psi@Strain 2.44 %, Temperature 248 °FISO 52767.28 MPa@Strain 2.84 %, Temperature 120 °C9758 psi